We report on two patients with fracture of a modular, tapered and distally fixed, uncemented titanium revision hip stem, not previously described. A failure analysis revealed that the cause of the fractures was the development of fatigue cracks in the mid-stem cobalt-chromium modular junction ending in corrosion-fatigue failure. No material defects or stress risers were found in any of the implant